HFFR (halogen free) flame retardant masterbatch for unfilled and filled PA (Nylon) UL94-V0

ProFlame®EFPA701/702/901/902 are made from halogen-free flame retardant and polyamide carrier with stabilizer and lubricant system .It is designed to eliminate the inhalation of dust and skin contact of powder in producing.

Benefits:
1.High temperature resistance, no halogen, no precipitation ,no frost spraying;
2.  Aging test (Temperature at 85℃ and the humidity 85%);
3.  excellent electrical performance;
4.  low corrosion of mold and screw.

Tech Spec:
Items                      PA701  PA702                     PA901 PA902
FR content(%)                 ≥70                                  ≥90
Appearance                              White granule
Moisture(%)                                     ≤0.3
Usage method           Direct injection molding or plastic modification
Dosage            19-24% for nylon-V0            14-19% for nylon-V0

Processing Guide:
►Before adding these FR masterbatch, it is generally not necessary to pre dry.
If there are special requirements for the moisture content of flame retardants, we recommend pre drying (such as drying at 100℃ for 4 hours).

►The optimal mixing conditions should depend on different
situations, and attention should be paid to ensure that all components
are evenly dispersed, and the processing and melting temperature of the polymer should not exceed 300 ℃.