micro-encapsulated red phosphorus masterbatch RP70

ProFlame® RP70 Masterbatch is made from micro-capsules encapsulated red phosphorus and polyamide or EVA carrier with stabilizer and lubricant system .It is designed to eliminate the inhalation of dust and skin contact of powder in producing and granule type also overcome disadvantage of easy to fire in storage and using are more secure.

RP70  Masterbatch can  be  incorporated to  a  polymer in  conjunction  with  flame

retardant and other additives directly. The Impact strength of polymers with this masterbatch is remarkably improved as compared to Red phosphorus powder.

Tech Spec:

Items	Spec
Micro encapsulated red phosphorus (%)	69.0-71.0
Appearance	granule
Moisture(%)	≤0.3
Density(g/cm3)	1.30-1.50
Melting point(℃)	140

Reference formula

Formula	PA66	RP70 masterbatch	fiberglass
Ratio	63%	7%	30%
Processing temperature	225℃
Performance	UL94V-0(1.6mm)

Recommended dosage :

PA6/PA66 glass fiber reinforced and toughened series with the dosage of 6-8%

Main features:

1. low dosage: for PA series added 6-9% , flame retardant properties can achieve

UL94 V-0(0.8mm) and tracking index (CTI) to 600V.

2.Good precipitation resistance: Fully coated red phosphorus from hydrophilic to hydrophobic surface from inorganic to organic, improved compatibility with resin. Especially precipitation resiatance migration capability is greatly improved.

3.Excellent mechanical properties: Less impact on the material properties and excellent mechanical properties of the parts because of low dosage .

4.High performance carrier : Absolutely guarantee the products of environmental protection and stability .

5.Fine particle size: RP70 uses fine grinding technology to producing finer particle size of micro-capsule red phosphorus, improved masterbatch dispersion, compatibility, precipitation resistance to make the product surface smooth and shining.

6.Environmental friendly non-halogen: Passing SGS test, meet ROHS requirements.

7.Good stability:Micro-capsule  coated  red  phosphorus  than  the  traditional masterbatch (not coated) has good chemical stability, improved the red phosphorus easy-absorption of moisture, the defects of easy-oxidation .